№ | Cathode composition, Me: С, ratio % per area | Coating phase composition, (X-ray)-wt% | Lattice type, parameters, nm | Crystal block size, nm | Microhar- Dness, GPa |
1 | 70Mo ÷ 30C | Mo2C-67; Mo-33; closer to the high temperature phase –β Mo2C | Hexagonal a = 0.301 c = 0.474 | Texture, 2.2 - 5.0 | 13.00 - 30.00 |
2 | 50Mo ÷ 50C | MoC – 95 ÷ 100; C(free) – 5 ÷ 0 | FCC α-MoC a = 0.427 | 6.0 - 8.0 | 18.00 - 31.00 |
3 | 70Nb ÷ 30C | Nb2C | Hexagonal a = 0.3115, c = 0.4948 | Texture, 1.0 - 3.0 | 23.00 - 29.00 |
4 | 50Nb ÷ 50C | NbC0.95-1.0 | FCK A = 0.443 | Texture, 2.2 - 5.0 | 18.90 - 23.00 |
5 | 50V ÷ 50C | VC0.85-0.88 | FCC a = 0.4188 | 1.5 - 5.0 | 13.00 - 26.00 |
6 | 50Zr ÷ 50C | ZrC0.5-0.6 – 76.5 ± 0.4 | Cubic B1-type 0.4683 | 5.0 - 6.0 | 18.50 - 30.00 |
7 | 80Zr ÷ 20C | ZrC0.9-0.95 – 96.5 ± 0.4; Zr – 23.5 ± 0.4 | Cubic B1-type 0.4683 | Texture, 0 - 18 | 10.00 - 21.00 |