Glass | Mole fraction of V2O5 | W | σ at 468 K | εp | WH | WP | WD |
| X | (eV) | (Ω·m)−1 |
| (eV) | (eV) | (eV) |
BPVN1 | 0.05 | 0.325 | 4.574 × 10−4 | 21.633 | 10.155 | 0.388 | 0.262 |
BPVN2 | 0.1 | 0.365 | 1.409 × 10−4 | 46.321 | 10.372 | 0.436 | 0.294 |
BPVN3 | 0.15 | 0.215 | 4.614 × 10−4 | 33.787 | 14.322 | 0.257 | 0.173 |
BPVN4 | 0.2 | 0.269 | 1.667 × 10−4 | 37.279 | 12.365 | 0.321 | 0.217 |
BPVN5 | 0.25 | 0.343 | 1.118 × 10−4 | 44.628 | 10.602 | 0.410 | 0.276 |
BPVN6 | 0.3 | 0.652 | 6.520 × 10−4 | 24.814 | 12.791 | 0.778 | 0.526 |
BPVN7 | 0.4 | 0.647 | 3.439 × 10−3 | 34.010 | 8.130 | 0.772 | 0.522 |
BPVN8 | 0.45 | 0.696 | 2.134 × 10−3 | 23.846 | 13.579 | 0.831 | 0.561 |