No. density (cm−3) | λf (nm) | FWHM (cm−1) | FI (A.U.) |
Method I | |||
6.78 × 1015 | 431 | 875 | 0.20 |
4.84 × 1016 | 431 | 975 | 0.45 |
8.52 × 1016 | 431 | 1265 | 0.59 |
3.80 × 1017 | 432 | 1386 | 0.82 |
8.56 × 1017 | 433 | 1274 | 0.69 |
2.49 × 1018 | 434 | 1170 | 0.49 |
5.51 × 1018 | 434 | 919 | 0.32 |
Method II | |||
4.96 × 1015 | 430 | 812 | 0.30 |
5.63 × 1016 | 430 | 990 | 0.52 |
9.51 × 1016 | 431 | 1206 | 0.78 |
3.78 × 1017 | 431 | 1379 | 0.90 |
7.96 × 1017 | 432 | 1219 | 0.75 |
2.71 × 1018 | 432 | 984 | 0.60 |
6.31 × 1018 | 433 | 829 | 0.42 |
Method III | |||
5.18 × 1015 | 432 | 753 | 0.51 |
3.94 × 1016 | 432 | 912 | 0.68 |
7.62 × 1016 | 432 | 1086 | 0.88 |
5.91 × 1017 | 433 | 1320 | 0.97 |
9.43 × 1017 | 433 | 1152 | 0.85 |
3.29 × 1018 | 434 | 1037 | 0.72 |
4.44 × 1018 | 434 | 896 | 0.51 |