F (wt.%) | Crystallite size D (nm) | Effective strain (%) | Lattice constants (Å) | TC(hkl) of plane | |||||
|
|
| a | Δa = a − a0 | c | Δc = c − c0 | (110) | (101) | (211) |
0 | 25.3 | 0.11 | 4.695 | −0.043 | 3.162 | −0.025 | 0.74 | 0.5 | 0.4 |
10 | / | / | / | / | / | / | / | / | / |
40 | 20 | 0.153 | 4.709 | −0.029 | 3.189 | 0.002 | 0.5 | 0.06 | 0.45 |
50 | 12.5 | 0.4 | 4.736 | −0.002 | 3.181 | −0.006 | 0.7 | 0.34 | 0.31 |