Optical Constants | |||||||
Sample | n | K (×10−4) | O.D. | O.C. (×1010) | ε' | ε'' (×10−3) | tan(δ) (×10−3) |
At λ = 500 nm (2.48 eV) | |||||||
Nd-0 | 1.001 | 0.128 | 0.042 | 0.766 | 1.002 | 0.026 | 0.025 |
Nd-2 | 1.032 | 0.895 | 0.292 | 5.542 | 1.066 | 0.185 | 0.173 |
Nd-4 | 1.038 | 1.169 | 0.323 | 7.274 | 1.076 | 0.243 | 0.225 |
At λ = 600 nm (2.066 eV) | |||||||
Nd-0 | 1.001 | 0.134 | 0.036 | 0.668 | 1.002 | 0.270 | 0.027 |
Nd-2 | 1.032 | 1.053 | 0.286 | 5.425 | 1.064 | 0.217 | 0.204 |
Nd-4 | 1.033 | 1.276 | 0.294 | 6.584 | 1.067 | 0.264 | 0.247 |
At λ = 700 nm (1.771 eV) | |||||||
Nd-0 | 1.001 | 0.143 | 0.033 | 0.614 | 1.001 | 0.290 | 0.029 |
Nd-2 | 1.030 | 1.192 | 0.278 | 5.256 | 1.061 | 0.246 | 0.231 |
Nd-4 | 1.029 | 1.384 | 0.273 | 6.097 | 1.060 | 0.285 | 0.269 |