Sample No | Axial Load, Ρ (kN) | Axial Stress, σ1 = P/A (MPa) | Confining Pressure, σ3 (MPa) | Material constant, mi | Friction Angle, φ (˚) | Apparent Cohesion, c (MPa) | Estimated Uniax. Compressive Strength, σciestm (Mpa) |
KP01A | 520 | 224.66 | 3 | 26.58 | 54.13 | 32.18 | 184.43 |
KP01B | 605 | 261.39 | 6 | ||||
KP01C | 857 | 370.26 | 18 | ||||
KP01D | 651 | 281.26 | 9 | ||||
KP02A | 573 | 247.56 | 3 | 28.16 | 54.78 | 35.54 | 206.44 |
KP02B | 609 | 263.12 | 6 | ||||
KP02C | 906 | 391.43 | 18 | ||||
KP02D | 809 | 349.53 | 9 | ||||
KS01A | 220 | 95.05 | 3 | 14.27 | 44.10 | 16.98 | 73.97 |
KS01B | 269 | 116.22 | 6 | ||||
KS01C | 338 | 146.03 | 12 | ||||
KS02A | 232 | 102.11 | 3 | 14.39 | 44.64 | 17.94 | 79.95 |
KS02B | 276 | 121.47 | 6 | ||||
KS02C | 350 | 154.04 | 12 | ||||
KS03A | 337 | 148.87 | 3 | 16.04 | 46.58 | 24.48 | 115.37 |
KS03B | 344 | 151.96 | 6 | ||||
KS03C | 539 | 238.11 | 18 | ||||
KS03D | 406 | 179.35 | 9 | ||||
OP01A | 284 | 122.70 | 3 | 21.09 | 48.17 | 20.96 | 95.89 |
OP01B | 369 | 159.43 | 6 | ||||
OP01C | 534 | 230.71 | 18 | ||||
OP01D | 398 | 171.95 | 9 | ||||
OP02A | 486 | 214.69 | 3 | 25.20 | 53.37 | 30.33 | 170.27 |
OP02B | 531 | 233.70 | 6 | ||||
OP02C | 789 | 348.54 | 18 | ||||
OP02D | 596 | 263.29 | 9 | ||||
OP03A | 582 | 250.53 | 3 | 27.76 | 55.01 | 33.85 | 200.41 |
OP03B | 609 | 262.15 | 6 | ||||
OP03C | 918 | 395.16 | 18 | ||||
OP03D | 726 | 312.51 | 9 | ||||
OP04A | 520 | 229.71 | 3 | 26.69 | 54.09 | 32.84 | 187.52 |