Experiment

Si [wt.%]

Cu [wt.%]

Sr [wt.%]

Ni [wt.%]

1

6 (A1)

3 (B1)

0.01 (C1)

0.5 (D1)

2

6 (A1)

5 (B2)

0.02 (C2)

1 (D2)

3

6 (A1)

7 (B3)

0.03 (C3)

1.5 (D3)

4

9 (A2)

3 (B1)

0.02 (C2)

1.5 (D3)

5

9 (A2)

5 (B2)

0.03 (C3)

0.5 (D1)

6

9 (A2)

7 (B3)

0.01 (C1)

1 (D2)

7

12 (A3)

3 (B1)

0.03 (C3)

1 (D2)

8

12 (A3)

5 (B2)

0.01 (C1)

1.5 (D3)

9

12 (A3)

7 (B3)

0.02 (C2)

0.5 (D1)