TOP PLASTER ETPS | TOP PLASTER ETPMK | TOP PLASTER ETP-T | TOP PLASTER ETPPF | |
(Fire resistant) filler | Feslag geopolymer | metakaolin geopolymer | Talc. Reference plaster already available, no filler | Aluminium hydroxide |
%w/w filler | 28% | 28% | 0% | 28% |
Total P.V.C % | 81.50 | 82.09 | 81.30 | 81.40 |
Emulsion | VAE | VAE | VAE | VAE |
%w/w emulsion (50% solids) | 14% | 14% | 14% | 14% |
Viscosity (cP) | 17,000 - 18,000 | 17,000 - 18,000 | 17,000 - 18,000 | 17,000 - 18,000 |
Density (gr/ml) | 1.770 | 1.740 | 1.760 | 1.750 |
Open time 0 - 5 (5 best/0 worst) | 5 | 5 | 5 | 4 |
Elasticity 0 - 5 (5 best/0 worst) | 4.5 | 4.5 | 5 | 5 |
Gloss (20˚/60˚/80˚) | 0.3/0.7/0.1 | 1.2/1.9/0.3 | 1.1/1.7/0.2 | 1.1/1.7/0.2 |
Alkali resistance | PASS | PASS | PASS | PASS |
ISO 834 fire test | PASS | PASS | FAIL | FAIL |
Carbonation protection (70 days CO2 penetration depth (mm)) | 8.50 | 1.90 | 4.90 | 3.80 |