Pb | V | Sc | Co | Ni | Cr | Y | Zr | Hf | Nb | Ta | Cs | Sr | Rb | Ba | |
SiO2 | −0.24 | 0.89 | 0.7 | 0.34 | 0.7 | −0.02 | 0.34 | 0.93 | 0.02 | 0.48 | 0.19 | 0.4 | −0.65 | 0.88 | −0.85 |
TiO2 | −0.15 | 0.89 | 0.68 | 0.27 | 0.64 | −0.15 | 0.29 | 0.91 | 0.12 | 0.47 | 0.24 | 0.43 | −0.7 | 0.86 | −0.77 |
Al2O3 | −0.14 | 0.96 | 0.57 | 0.21 | 0.61 | −0.07 | 0.2 | 0.94 | 0.1 | 0.36 | 0.09 | 0.57 | −0.69 | 0.83 | −0.83 |
MgO | 0.69 | 0.01 | −0.78 | −0.93 | −0.81 | −0.74 | −0.88 | −0.4 | 0.66 | −0.69 | −0.28 | 0.59 | −0.3 | −0.59 | 0.6 |
CaO | 0.19 | −0.85 | −0.72 | −0.3 | −0.66 | 0.15 | −0.34 | −0.88 | −0.09 | −0.5 | −0.28 | −0.35 | 0.69 | −0.86 | 0.76 |
Na2O | 0.64 | −0.3 | 0.44 | 0.39 | 0.36 | 0.11 | 0.54 | 0.14 | 0.61 | 0.71 | 0.95 | −0.18 | 0.43 | 0.31 | 0.42 |
K2O | −0.09 | 0.98 | 0.39 | −0.05 | 0.38 | −0.33 | −0.04 | 0.81 | 0.18 | 0.15 | −0.04 | 0.66 | −0.86 | 0.67 | −0.73 |
P2O5 | 0.5 | −0.68 | −0.84 | −0.6 | −0.82 | −0.21 | −0.59 | −0.84 | 0.28 | −0.61 | −0.23 | −0.03 | 0.43 | −0.88 | 0.89 |
LOI | 0.12 | −0.96 | −0.44 | −0.17 | −0.56 | −0.04 | −0.12 | −0.92 | −0.08 | −0.26 | 0.04 | −0.67 | 0.61 | −0.76 | 0.84 |
Ba | 0.63 | −0.75 | −0.56 | −0.45 | −0.67 | −0.32 | −0.35 | −0.78 | 0.45 | −0.3 | 0.17 | −0.21 | 0.43 | −0.72 | |
Rb | −0.11 | 0.64 | 0.9 | 0.67 | 0.93 | 0.29 | 0.69 | 0.95 | 0.08 | 0.82 | 0.54 | 0.18 | −0.25 | ||
Sr | 0.06 | −0.81 | −0.03 | 0.46 | 0.08 | 0.71 | 0.43 | −0.41 | −0.2 | 0.24 | 0.26 | −0.61 | |||
Cs | 0.46 | 0.74 | −0.24 | −0.52 | −0.13 | −0.41 | −0.53 | 0.46 | 0.57 | −0.28 | −0.23 | ||||
Ta | 0.44 | −0.12 | 0.69 | 0.54 | 0.56 | 0.11 | 0.69 | 0.33 | 0.49 | 0.86 | |||||
Nb | 0.02 | 0.09 | 0.93 | 0.86 | 0.9 | 0.46 | 0.93 | 0.62 | 0.1 | ||||||
Hf | 0.96 | 0.17 | −0.08 | −0.38 | −0.15 | −0.53 | −0.24 | 0.15 | |||||||
Zr | −0.05 | 0.82 | 0.73 | 0.47 | 0.81 | 0.19 | 0.46 | ||||||||
Y | −0.26 | −0.09 | 0.89 | 0.98 | 0.89 | 0.68 | |||||||||
Cr | −0.39 | −0.24 | 0.37 | 0.79 | 0.59 | ||||||||||
Ni | −0.27 | 0.37 | 0.94 | 0.9 | |||||||||||
Co | −0.38 | −0.06 | 0.84 | ||||||||||||
Sc | −0.24 | 0.31 | |||||||||||||
V | −0.07 |