x (wt%) | Relative volume fraction (%) | Lattice parameters (Å) | Experimental density | Porosity | |||
Gd-123 | BaCuO2 | a | b | c | ρ (kg/m3) | P (%) | |
0.0 | 97.36 | 2.64 | 3.842 | 3.895 | 11.69 | 4881 | 29.97 |
(ZnFe2O4)xGdBa2Cu3O7−δ | |||||||
0.01 | 97.68 | 2.32 | 3.842 | 3.895 | 11.697 | 4881 | 29.97 |
0.02 | 97.78 | 2.22 | 3.848 | 3.900 | 11.708 | 5041 | 27.41 |
0.04 | 97.82 | 2.18 | 3.845 | 3.896 | 11.705 | 5316 | 23.62 |
0.06 | 98.39 | 1.61 | 3.851 | 3.900 | 11.702 | 5370 | 22.68 |
0.1 | 96.30 | 3.70 | 3.842 | 3.892 | 11.696 | 5463 | 21.74 |
0.2 | 95.86 | 4.14 | 3.85 | 3.901 | 11.705 | 5425 | 21.91 |
0.4 | 95.64 | 4.36 | 3.847 | 3.866 | 11.706 | 5219 | 25.59 |
(CoFe2O4)xGdBa2Cu3O7−δ | |||||||
0.01 | 98.33 | 1.67 | 3.848 | 3.897 | 11.700 | 5275 | 24.14 |
0.02 | 97.87 | 2.13 | 3.842 | 3.895 | 11.690 | 5299 | 24.03 |
0.04 | 97.67 | 2.33 | 3.844 | 3.895 | 11.700 | 5317 | 22.06 |
0.06 | 97.52 | 2.48 | 3.842 | 3.893 | 11.700 | 5464 | 21.64 |
0.1 | 96.00 | 4.00 | 3.848 | 3.895 | 11.700 | 5537 | 20.42 |
0.2 | 95.52 | 4.48 | 3.844 | 3.896 | 11.690 | 5592 | 19.76 |
0.4 | 95.21 | 4.86 | 3.847 | 3.904 | 11.690 | 5658 | 18.68 |