Compound | Range of T | θ | Qb |
[K] | [kJ・mol−1] | ||
α-FeHx (bcc) | <1175 | >0.01 | −171 |
γ-FeHx (fcc) | 1185 - 1590 | (0.50)a | −138 |
δ-FeHx (bcc) | 1665 - 1715 | (0.50)a | −100 |
α-FeCx (bcc) | <1000 | >0.10 | −648 |
α-FeCx (bcc) | 1025 - 1150 | >0.10 | −613 |
γ-FeCx (fcc) | 1175 - 1575 | 0.20 | −679 |
FeCx (molten) | 1550 - 1775 | 1.00 | −699 |
α-FeNx (bcc) | <1115 | >0.05 | −420 |
γ-FeNx (fcc) | 1250 - 1625 | (0.50)a | −455 |
δ-FeNx (bcc) | 1675 - 1715 | (0.50)a | −352 |
FeNx (molten) | 1850 - 2000 | >0.10 | −427 |
FePx (molten) | 1475 - 1775 | 0.50 | −347 |
FeSx (molten) | 1775 - 1875 | 1.00 | −307 |