Sample | 2θ110 (˚) | 2θ200 (˚) | 2θ002 (˚) | d110 (nm) | d200 (nm) | d002 (nm) | L110 (nm) | L200 (nm) | L002 (nm) | β110 (nm) | β200 (nm) | β002 (nm) |
G-Exp | - | - | 26.15 | - | - | 0.34 | - | - | 5.12 | - | - | 1.7720 |
GO | - | - | 25.61 | - | - | 0.35 | - | - | 4.24 | - | - | 2.1973 |
BATCH1 | 21.71 | 24.06 | 26.39 | 0.41 | 0.37 | 0.34 | 22.50 | 18.61 | 5.73 | 0.3997 | 0.4853 | 1.5844 |
BATCH2 | 22.38 | 24.78 | 27.24 | 0.40 | 0.36 | 0.33 | 9.32 | 13.19 | 2.40 | 0.9658 | 0.6858 | 3.7854 |
BATCH3 | 21.63 | 23.98 | 26.61 | 0.41 | 0.42 | 0.34 | 24.44 | 21.46 | 33.81 | 0.3680 | 0.4208 | 0.2685 |