Polymer | Conc. g∙cm−3 | ηr | 40˚C | 100˚C |
Rg/nm (Porod Exp. n) | Rg/nm (Porod Exp. n) | |||
OCP2 | 0.0018 | 1.15 | 13.4 ± 0.2 (1.79) | 11.9 ± 0.3 (1.79) |
0.0029 | 1.25 | 13.8 ± 1.0 (1.78) | 11.8 ± 0.8 (1.79) | |
0.0059 | 1.50 | 10.9 ± 0.3 (1.80) | 10.6 ± 0.4 (1.76) | |
0.0100 | 2.00 | 9.9 ± 0.3 (1.76) | 9.7 ± 0.3 (1.72) | |
0.0210 | 4.00 | 7.5 ± 0.1 (1.71) | 6.9 ± 0.1 (1.72) | |
PMA3 | 0.0038 | 1.15 | 11.3 ± 0.1 (2.00) | 14.4 ± 0.5 (1.76) |
0.0083 | 1.25 | 10.9 ± 0.1 (2.00) | 11.9 ± 0.2 (1.82) | |
0.0148 | 1.50 | 10.1 ± 0.1 (2.00) | 10.3 ± 0.1 (1.83) | |
0.0296 | 2.00 | 8.8 ± 0.1 (2.00) | 7.7 ± 0.1 (1.87) | |
0.0706 | 4.00 | 6.5 ± 0.1 (2.00) | 4.9 ± 0.1 (1.98) |