Sample | Tensile Strength (MPa) | Tensile Modulus (MPa) | Elongation at UTS (mm) | Flexural Strength (MPa) | Flexural Modulus (MPa) | Impact Energy (J) | Impact strength (KJ/m2) | Hardness (Shore D) |
FA0 | 9.06 | 213.35 | 134.30 | 18.54 | 353.6 | 0.21 | 2.88 | 90 |
FA-F6 | 9.11 | 219.72 | 32.78 | 17.47 | 576.15 | 0.15 | 2.07 | 91 |
FA-C6 | 12.05 | 257.52 | 29.35 | 35.83 | 652.52 | 0.19 | 2.71 | 91 |
FA-F40 | 11.52 | 365.75 | 19.96 | 21.18 | 1180.5 | 0.11 | 1.57 | 94 |
FA-C40 | 10.26 | 483.14 | 15.57 | 30.94 | 1163.3 | 0.10 | 1.52 | 94 |