Glass systems | σ (S∙cm−1) at 25˚C | References |
30LiI-41Li2O-29P2O5 | 3.0 × 10−6 | A. Chandra et al. [52] |
0.2LiBr-0.48Li2O-0.32P2O5 | 2.72 × 10−6 | T. Thieu Duc et al. [189] |
30LiCl-35Li2O-35P2O5 | 1.0 × 10−7 | J.P. Maligani et al. [190] |
12.3LiCl-31.8Li2O-59.9B2O3 | 3.2 × 10−6 | A.R. Kulkarni et al. [191] |
Li3.3PO3.8N0.22 | 3.3 × 10−6 | X.H. Yu et al. [181] |
0.24Li2S-0.36GeS2-0.36LiI-0.04LiBr | 2.0 × 10−4 | B. Carret et al. [145] |
0.36GeS2-0.24Li2S-0.40LiI | 1.2 × 10−4 | T. Minami et al. [149] |
45LiI-37Li2S-18P2S5 | 1.0 × 10−3 | J.P. Malugani et al. [192] |
63Li2S-36SiS2-Li3PO4 | 1.5 × 10−3 | N. Aotani et al. [134] |
50Li2S-17P2S5-33LiBH4 | 1.6 × 10−3 | A. Yamauchi et al. [170] |
30Li2S-26B2S3-44LiI | 1.7 × 10−3 | H. Wada et al. [106] |
0.57Li2S-0.38SiS2-0.05Li4SiO4 | 2.0 × 10−3 | K. Hirai et al. [193] |
0.24Li2S-0.36GeS2-0.40LiI | 1.2 × 10−4 | Y. Kim et al. [130] |
0.526Li2S-0.211GeS2-0.25SiS2 | 1.7 × 10−4 | M. Yamashita et al. [194] |
0.48Li2S-0.48GeS2-0.04Li4SiO4 | 3.4 × 10−4 | T. Minami et al. [149] |
0.58Li2S-0.39GeS2-0.03Li3PO4 | 3.0 × 10−4 | Y. Yamamura et al. [148] |
(60-3x/2)Li2S-40SiS2-xLi3N (x = 3) | 1.5 × 10−3 | R. Sakamoto et al. [183] |
Li3OCl | 1.2 × 10−1 | M.H. Braga et al. [186] |