structure | Calculated M.W | Calculated M.W +Na | Experimental peak | Peak relative proportion (%) | |
G -5H | Monomer | 177 | 200 | 200 | 85 |
G -4H | Monomer | 193 | 216 | 216 | 8 |
H-G + 12H | dimer | 257 | 280 | 280 | 12 |
G-H + 1H | dimer | 277 | 300 | 300 | 5 |
S-H-10H | dimer | 339 | 362 | 362 | 18 |
S-H +4H | dimer | 353 | 376 | 376 | 5 |
S-S-OH | dimer | 419 | 442 | 442 | 5 |
S-S-H-1H | trimer | 528 | 551 | 551 | 10 |
S-S-S-2H | trimer | 628 | 651 | 651 | 3 |
H-G-H-G + 11H | tetramer | 689 | 712 | 712 | 3 |
G-G-G-S + 1H | tetramer | 751 | 774 | 774 | 65 |
S-S-S-S-S-S | hexamer | 998 | 1021 | 1021 | 45 |
S-H-S-H-S-H-1H | hexamer | 1060 | 1083 | 1083 | 28 |
S-H-S-H-S-H-4H | hexamer | 1073 | 1096 | 1096 | 100 |
S-H-S-H-S-H-S-H-4H | octamer | 1336 | 1359 | 1359 | 82 |
S-S-S-S-S-S-S-S-2H | heptamer | 1468 | 1491 | 1491 | 70 |
S-H-S-H-S-H-S-H-S-H | decamer | 1600 | 1623 | 1623 | 60 |
G-S-G-S-G-S-G-S -CH3-OH | octamer | 1732 | 1755 | 1755 | 42 |
G-G-G-G-G-G-G-G-G-G + H2O | decamer | 1864 | 1887 | 1887 | 35 |
H-S-H-S-H-S-H-S-H-S-H-S-H-S-1H | pentadecamer | 2127 | 2150 | 2150 | 22 |
H-G-H-G-H-G-H-G-H-G-H-G-H-G + H2O | tetradecamer | 2391 | 2414 | 2414 | 18 |
G-G-G-G-G-G-G-G-G-G-G-G-G-G-G-G-G-G | octadecamer | 2655 | 2678 | 2678 | 10 |
S-S-S-S-S-S-S-S-S-S-S-S-S-S + CH3 | tetradecamer | 2918 | 2941 | 2941 | 10 |
S-H-S-H-S-H-S-H-S-H-S-H-S-H-S-H-S-H + 6H | octadecamer | 3183 | 3206 | 3206 | 8 |
G-S-G-S-G-S-G-S-G-S-G-S-G-S-G-S-OH | hexadecamer | 3447 | 3470 | 3470 | 3 |
G-S-G-S-G-S-G-S-G-S-G-S-G-S-G-S-G-S + Na+ | octadecamer | 3712 | 3735 | 3735 | 5 |