Head Diameter (mm) | Head Material | HXLPE Brand | Mean Wear Rate (mm/year) | Source |
28 | Co-Cr (3) | Crossfire (2) | 0.12 | Martell et al. [2] |
28 | Co-Cr (3) | Marathon (6) | 0.08 | Hopper et al. [3] |
28 | Co-Cr (3) | Crossfire (2) | 0.05 | Krushell et al. [4] |
28 | Co-Cr (3) | Crossfire (2) | 0.036 | D’Antonio et al. [5] |
28 | Co-Cr (3) | Longevity (5) | 0.018 | Manning et al. [6] |
28 | Co-Cr (3) | Durasul (3) | 0.010 | Manning et al. [6] |
28 | Co-Cr (3) | Durasul (3) | 0.029 | Dorr et al. [7] |
28 | Co-Cr (3) | Marathon (6) | 0.010 | Engh et al. [8] |
32 | Co-Cr (3) | Durasul (3) | 0.010 | Bragdon et al. [9] |
28 | Al2O3 (1) | Aeonian (1) | 0.006 | Oonishi et al. [10] |
28 | Co-Cr (3) | Marathon (6) | 0.010 | Leung et al. [12] |
28 | Co-Cr (3) | Crossfire (2) | 0.006 | Rohrl et al. [13] |
28 | Co-Cr (3) | Durasul (3) | 0.025 | Triclot et al. [14] |
28 | Co-Cr (3) | Longevity (5) | 0.050 | Olyslaegers et al. [15] |
28 | Co-Cr (3) | Longevity (5) | 0.030 | Glynn-Jones et al. [16] |
28 | Co-Cr (3) | Marathon (6) | 0.031 | Bitsch et al. [17] |
28 | Oxinium (4) | Longevity (5) | 0.004 | Garvin et al. [18] |
28 | Co-Cr (3) | Crossfire (2) | 0.022 | Rajadhyaksa et al. [19] |
28 | Co-Cr (3) | Marathon (6) | 0.0239 | Calvert et al. [20] |
28 | Al2O3 (1) | Marathon (6) | 0.060 | Kim et al. [21] |
28 | Co-Cr (3) | Duration (4) | 0.088 | Geerdink et al. [22] |
22.225 | ZrO2 (6) | Aeonian (1) | 0.067 | Ise et al. [24] |
22.225 | Stainless Steel (5) | Aeonian (1) | 0.068 | Ise et al. [24] |
26 | Co-Cr (3) | Aeonian (1) | 0.010 | Kawate et al. [25] |
26 | ZrO2 (6) | Aeonian (1) | 0.000 | Kawate et al. [25] |
28 | Co-Cr (3) | Longevity (5) | 0.028 | Lachiewicz et al. [28] |
28 | Co-Cr (3) | Marathon (6) | 0.007 | Campbell et al. [29] |
26 | ZrO2 (6) | Longevity (5) | 0.010 | Fukui et al. [30] |
28 | Co-Cr (3) | Reflection (7) | 0.026 | Whittaker et al. [31] |
28 | Co-Cr (3) | Longevity (5) | 0.025 | Whittaker et al. [31] |
44 | Co-Cr (3) | Durasul (3) | 0.021 | Hammerberg et al. [32] |
26 | Co-Cr (3) | Longevity (5) | <0.001 | Nakahara et al. [33] |
26 | ZrO2 (6) | Longevity (5) | <0.001 | Nakahara et al. [33] |
28 | Co-Cr (3) | Marathon (6) | 0.050 | Mutimer et al. [35] |