Investigators | Year | Temperature range, K | Hydrogen solubility constants | H solubility, cm3/100g | Sample conditions | ||
A | B | 773 K | 823 K | ||||
Ransley and Neufeld | 1947 | 738 - 893 | −1942.20 | 0.628 | 0.013 | 0.018 | Cold rolled |
Eichenauer and Pebler | 1957 | 743 - 863 | −4088.60 | 3.148 | 0.007 | 0.015 | Cast ingot |
Eichenauer et al. | 1961 | 633 - 873 | −2942.50 | 1.815 | 0.010 | 0.017 | As-cast |
Pmenov | 1967 | 683 - 878 | −1783.60 | 0.452 | 0.014 | 0.019 | ? |
Eichenauer | 1968 | 758 - 891 | −3347.40 | 2.155 | 0.007 | 0.012 | Extruded bar |
Zhukhovitsky et al. | 1972 | 823 | - | - | - | 0.062 |
|
Gelman | 1972 | 823 | - | - | - | 0.026 | ? |
Gabidullin et al. | 1974 | 773 - 923 | −1901.00 | 0.663 | 0.016 | 0.023 |
|
Gabidullin et al. | 1973 | 673 - 933 | −1695.50 | 0.394 | 0.016 | 0.022 |
|
Levchuk et al. | 1974 | 698 - 848 | −1847.70 | 0.509 | 0.013 | 0.018 |
|
Andreev et al. | 1976 | 773, 823 | −4300.00 | 3.325 | 0.006 | 0.013 | Extruded rod, |
Ichimura et al. | 1979 | 723 - 909 | −3360.90 | 2.237 | 0.008 | 0.014 | Vacuum melted |
673 - 920 | −2081.60 | 0.777 | 0.012 | 0.018 | Air melted | ||
Ichimura & Imabayashi | 1980 | 673 - 913 | −981.40 | 0.066 | 0.063 | 0.075 | Air melted |
Hashimoto and Kino | 1983 | 621 - 661 | −4901.00 | 4.790 | 0.028 | 0.068 |
|
Cogan et al. | 1987 | 673 - 903 | −5931.90 | 4.884 | 0.002 | 0.005 |
|
Ichimura et al. | 1991 | 723 - 903 | −2945.10 | 1.735 | 0.008 | 0.014 | Single grain |
773 - 903 | −3400.53 | 2.235 | 0.007 | 0.013 | Equiaxed grain | ||
Anyalebechi | 1992 | 773, 823 | −1975.70 | 0.753 | 0.016 | 0.022 | Extruded rod |
Ichimura et al. | 1992 | 673 - 873 | −3063.10 | 1.908 | 0.009 | 0.015 | Vacuum melted |
−1215.60 | −0.305 | 0.013 | 0.017 | Air melted | |||
−625.21 | −0.971 | 0.017 | 0.019 | As-cast ingot | |||
Ichimura and Sasajima | 1993 | 673 - 825 | −3233.99 | 2.368 | 0.013 | 0.023 | Air melted, 0.05 wt.% Ti |
673 - 826 | −3301.00 | 2.411 | 0.014 | 0.025 | N2 melted, 0.05 wt.% Ti | ||
673 - 827 | −2707.60 | 1.629 | 0.013 | 0.022 | Air melted, 0.10 wt.% Ti | ||
673 - 828 | −2707.60 | 2.182 | 0.021 | 0.037 | N2 melted with 0.10 wt.% Ti |