| J. Alam et al. (2013) | J.N Akhtar et al. (2010) | |||||
| Mould Designation | Compressive Strength (MPa) | K27 (m/s) | Mould Designation | Compressive Strength (MPa) | Mould Designation | Compressive Strength (MPa) |
| 00FABT 05FABT 10FABT 15FABT 20FABT | 3.636 3.688 3.755 3.940 3.690 | 18.45 × 10−7 17.60 × 10−7 16.00 × 10−7 14.70 × 10−7 18.10 × 10−7 | 00FAB 05FAB 10FAB 15FAB 20FAB | 3.348 3.690 4.390 5.385 4.450 | 00FALSDB1 05FALSDB2 10FALSDB3 15FALSDB4 20FALSDB5 | 3.666 4.235 7.156 6.569 4.790 |
| 00TFABT 05TFABT 10TFABT 15TFABT 20TFABT | 4.055 4.100 4.310 4.535 4.315 | 14.65 × 10−7 14.05 × 10−7 13.85 × 10−7 12.75 × 10−7 12.95 × 10−7 | 00FRFAB 05FRFAB 10FRFAB 15FRFAB 20FRFAB | 3.748 3.990 4.790 6.350 4.750 | 00FRFALSDB1' 05FRFALSDB2' 10FRFALSDB3' 15FRFALSDB4' 20FRFALSDB5' | 3.666 4.235 8.156 6.569 4.790 |
| 00TFASDBT 05TFASDBT 10TFASDBT 15TFASDBT 20TFASDBT | 4.845 5.300 5.480 5.900 5.714 | 23.50 × 10−7 22.50 × 10−7 20.40 × 10−7 17.80 × 10−7 23.10 × 10−7 | 00FALB 05FALB 10FALB 15FALB 20FALB | 3.685 4.065 4.865 6.599 4.596 | 10FALSDB6 15FALSDB7 20FALSDB8 25FALSDB9 30FALSDB10 | 8.160 8.330 8.520 8.890 7.480 |
| 10TFASDBT 15TFASDBT 20TFASDBT 25TFASDBT 30TFASDBT | 4.690 6.896 6.240 5.770 5.390 | 23.30 × 10−7 14.97 × 10−7 17.53 × 10−7 20.75 × 10−7 22.29 × 10−7 | 00FRFALB 05FRFLAB 10FRFALB 15FRFALB 20FRFALB | 4.185 5.465 5.850 7.859 5.460 | 10FRFALSDB6' 15FRFALSDB7' 20FRFALSDB8' 25FRFALSDB9' 30FRFALSDB10' | 8.315 8.545 8.625 9.155 7.755 |