Polymer kPQ (nm) | λ(emiss.) | Plasticizer (%) | Time (min.) | R2 |
| |
PS | 327 | DMT, 0.0% | 180 | 0.993 | 2.129 | 0.0062 |
PS | 329 | DMT, 1.0% | 180 | 0.996 | 2.004 | 0.0056 |
PS | 331 | DMT, 2.0% | 180 | 0.988 | 1.913 | 0.0050 |
PS | 333 | DMT, 3.0% | 180 | 0.993 | 1.802 | 0.0047 |
PS | 334 | DMT, 4.0% | 180 | 0.992 | 1.660 | 0.0035 |
PS | 327 | DET, 0.0% | 180 | 0.971 | 2.051 | 0.0058 |
PS | 328 | DET, 1.0% | 180 | 0.987 | 1.955 | 0.0053 |
PS | 332 | DET, 2.0% | 180 | 0.994 | 1.809 | 0.0044 |
PS | 333 | DET, 3.0% | 180 | 0.994 | 1.710 | 0.0040 |
PS | 336 | DET, 4.0% | 180 | 0.991 | 1.552 | 0.0027 |
PS | 327 | DOT, 0.0% | 180 | 0.998 | 2.584 | 0.0089 |
PS | 331 | DOT, 1.0% | 180 | 0.994 | 2.510 | 0.0084 |
PS | 338 | DOT, 2.0% | 180 | 0.998 | 2.402 | 0.0077 |
PS | 342 | DOT, 3.0% | 180 | 0.984 | 2.214 | 0.0067 |
PS | 344 | DOT, 4.0% | 165 | 0.978 | 1.755 | 0.0039 |
PS | 327 | DBP, 0.0% | 180 | 0.930 | 1.941 | 0.0052 |
PS | 329 | DBP, 1.0% | 180 | 0.935 | 1.889 | 0.0048 |
PS | 330 | DBP, 2.0% | 180 | 0.949 | 1.800 | 0.0042 |
PS | 333 | DBP, 3.0% | 180 | 0.995 | 1.702 | 0.0036 |
PS | 334 | DBP, 4.0% | 180 | 0.968 | 1.561 | 0.0030 |
PS | 327 | DOP, 0.0% | 180 | 0.9595 | 1.945 | 0.0053 |
PS | 328 | DOP, 1.0% | 180 | 0.994 | 1.775 | 0.0044 |
PS | 330 | DOP, 2.0% | 180 | 0.973 | 1.523 | 0.0028 |
PS | 331 | DOP, 3.0% | 180 | 0.993 | 1.420 | 0.0023 |
PS | 332 | DOP, 4.0% | 180 | 0.978 | 1.374 | 0.0021 |