Sl. No | Solutionizing time (A) | Aging temperature (B) | Aging time (C) | Tensile strength (Mpa) | Yield strength (Mpa) | Micro hardness |
1 | 4 | 190 | 7 | 195 | 181 | 54 |
2 | 2 | 190 | 7 | 216 | 188 | 59 |
3 | 4 | 150 | 7 | 174 | 161 | 66 |
4 | 2 | 150 | 7 | 164 | 157 | 49 |
5 | 4 | 190 | 3 | 166 | 143 | 49 |
6 | 2 | 190 | 3 | 174 | 156 | 66 |
7 | 4 | 150 | 3 | 205 | 172 | 59 |
8 | 2 | 150 | 3 | 180 | 173 | 53 |
9 | 5 | 170 | 5 | 123 | 113 | 49 |
10 | 1 | 170 | 5 | 124 | 121 | 50 |
11 | 3 | 130 | 1 | 159 | 137 | 54 |
12 | 3 | 130 | 5 | 150 | 140 | 55 |
13 | 3 | 210 | 9 | 189 | 161 | 54 |
14 | 3 | 170 | 1 | 200 | 174 | 60 |
15 | 3 | 170 | 5 | 254 | 225 | 64 |
16 | 3 | 170 | 5 | 257 | 227 | 63 |
17 | 3 | 170 | 5 | 254 | 224 | 62 |
18 | 3 | 170 | 5 | 257 | 221 | 63 |
19 | 3 | 170 | 5 | 258 | 225 | 64 |
20 | 3 | 170 | 5 | 257 | 226 | 65 |