Fiber diameter | Properties | E2 Corrgram values | Treated E2 Corrgram values | E4 Corrgram values | Treated E4 Corrgram values |
Average length (cm) | 0.07 | −0.08 | 0.09 | 0.04 | |
Elongation at break (%) | 0.07 | −0.12 | −0.17 | −0.03 | |
Contact angle (˚) | 0.03 | −0.29 | −0.03 | −0.01 | |
Tensile stress (MPa) | −0.57 | −0.37 | −0.38 | −0.24 | |
Young’s modulus (GPa) | −0.66 | −0.50 | −0.48 | −0.43 | |
Aspect ratio (L/D) | −0.75 | −0.68 | −0.50 | −0.50 | |
Load at break (N) | 0.34 | 0.24 | 0.01 | 0.02 | |