% sugarcane molasses | Volumic mass (kg/m3) | Flexural strength (MPa) | Flexural modulus of elasticity (MPa) | Compressive strength (MPa) | Modulus of elasticity in compression (MPa) | Thermal conductivity (W/mK) |
12 | 169 ± 12 | 0.4899 ± 0.201 | 39.6 ± 8.1 | 0.198 ± 0.044 | 7 ± 2 | 0.0709 ± 0.0017 |
14 | 171 ± 9 | 0.292 ± 0.032 | 25.1 ± 6.8 | 0.269 ± 0.010 | 4 ± 0 | 0.0690 ± 0.0017 |
16 | 176 ± 14 | 0.896 ± 0.032 | 53.2 ± 2.7 | 0.360 ± 0.063 | 16 ± 2 | 0.0688 ± 0.0025 |
18 | 179 ± 10 | 0.925 ± 0.101 | 81.7 ± 1.43 | 0.430 ± 0.019 | 19 ± 3 | 0.0721 ± 0.0023 |
20 | 193 ± 11 | 0.871 ± 0.1088 | 44.9 ± 1.1 | 0.062 ± 0.060 | 12 ± 1 | 0.0755 ± 0.0030 |
22 | 203 ± 10 | 0.947 ± 0.063 | 37.7 ± 1.9 | 0.741 ± 0.069 | 7 ± 0 | 0.0754 ± 0.0021 |
24 | 199 ± 16 | 1.428 ± 0.228 | 83.5 ± 1.12 | 0.450 ± 0.024 | 20 ± 1 | 0.0846 ± 0.0033 |
26 | 214 ± 12 | 1.774 ± 0.203 | 150.01 ± 2.5 | 1.016 ± 0.168 | 37 ± 6 | 0.0818 ± 0.0034 |
28 | 196 ± 12 | 1.273 ± 0.025 | 105 ± 25 | 0.631 ± 0.052 | 17 ± 1 | 0.0785 ± 0.0030 |
30 | 186 ± 11 | 1.030 ± 0.230 | 82.8 ± 9.2 | 0.518 ± 0.070 | 16 ± 2 | 0.0793 ± 0.0022 |