Complexes | λex/nm | complex powders λem/nm (relative intensity) | in silica gel λem/nm (relative intensity) | ||||||
|
| 5D0 → | I calc | Iexp | Iexp?I calc | 5D0 → | I calc | Iexp | Iexp/I calc |
Gd2L | 382 | 614.5 | 0 | 0 |
| 614.0 | 0 | 0 |
|
Eu0.2Gd1.8L | 383 | 614.5 | 10 | 38 | 3.8 | 614.0 | 10 | 27 | 2.7 |
Eu0.6Gd1.4L | 383 | 614.5 | 30 | 96 | 3.2 | 614.0 | 30 | 75 | 2.5 |
Eu0.8Gd1.2L | 383 | 614.0 | 40 | 121 | 3.0 | 614.0 | 40 | 89 | 2.2 |
Eu1.0Gd1.0L | 383 | 614.0 | 50 | 135 | 2.7 | 613.5 | 50 | 98 | 2.0 |
Eu1.2Gd0.8L | 382 | 614.0 | 60 | 128 | 2.1 | 613.5 | 60 | 102 | 1.7 |
Eu1.4Gd0.6L | 382 | 614.0 | 70 | 112 | 1.6 | 613.5 | 70 | 105 | 1.5 |
Eu1.6Gd0.4L | 382 | 614.0 | 80 | 107 | 1.3 | 613.5 | 80 | 103 | 1.3 |
Eu1.8Gd0.2L | 381 | 614.0 | 90 | 102 | 1.1 | 613.5 | 90 | 101 | 1.1 |
Eu2L | 382 | 613.5 | 100 | 100 | 1.0 | 613.5 | 100 | 100 | 1.0 |