Measure | Masterbatch | Strength 100a (N) | Ultimate length (mm) | Elongation at break (%) | Strength at break (N) | Stress at break (MPa) | Modulus at break (MPa) | Modulus 100b (MPa) |
Mean value | A | 19.2 | 74.9 | 299 | 51.6 | 3.49 | 1.16 | 1.30 |
B | 17.5 | 56.8 | 227 | 33.3 | 2.25 | 1.00 | 1.18 | |
C | 25.2 | 61.2 | 245 | 48.3 | 3.27 | 1.36 | 1.70 | |
STDc | A | 1.0 | 10.8 | 43 | 9.6 | 0.65 | 0.09 | 0.07 |
B | 2.2 | 9.1 | 36 | 3.8 | 0.26 | 0.08 | 0.15 | |
C | 2.9 | 13.0 | 52 | 7.9 | 0.54 | 0.16 | 0.20 | |
CoVd (%) | A | 5.2 | 14.4 | 14.4 | 18.6 | 18.6 | 5.63 | 5.38 |
B | 12.6 | 16.0 | 15.9 | 11.4 | 11.6 | 8.00 | 12.7 | |
C | 11.5 | 21.2 | 21.2 | 16.4 | 16.5 | 11.76 | 11.76 |