Ingredient | Masterbatch formulation | |
Concentration (pphr) | Quantity (g) | |
NR, 50a | 1/4 | 100 |
Inner tube crumb | 3/4 | 300 |
Zinc oxide | 4.0 | 16 |
Stearic acid | 1.25 | 5 |
Sulphur | 2.5 | 10 |
TMTD | 0.75 | 3 |
N330 | 50 | 200 |
Vulkacit H/30 | 3 | 12 |
Vulcanization temperature | Processing parameters | 150˚C |
Optimun cure time | Mechanical properties | 4.9 minutes |
Developed material | Manufactured products | |
Hardness (Shore A) | 60.4 ± 0.5 | 50 to 90 |
Elongation at break (%) | 319 ± 36 | 300 to 1000 |
Stress at break (MPa) | 3.82 ± 0.64 | 3 to 20 |
Modulus 100b (MPa) | 1.42 ± 0.16 | 1 to 4 |
Modulus at break (MPa) | 1.19 ± 0.10 | - |