t [min] = 15 | t [min] = 30 | |||
MβCD [μM] | 0 β-A | 2.5 β-A | 0 β-A | 2.5 β-A |
0 | 111.5 ± 0.8 | 150 ± 30 | 118.2 ± 1.5 | 150 ± 30 |
0.5 | 110.5 ± 2.4 | 195 ± 14 | 114.8 ± 2.0 | 206 ± 9 |
1 | 112 ± 4 | 174 ± 16 | 115 ± 6 | 175 ± 14 |
1.5 | 111.4 ± 1.0 | 182 ± 4 | 116.5 ± 1.0 | 192 ± 7 |
2 | 111.7 ± 1.0 | 176 ± 22 | 117.7 ± 2.2 | 182 ± 26 |
2.5 | 119 ± 8 | 168 ± 15 | 122 ± 8 | 178 ± 20 |
t [min] = 45 | t [min] = 60 | |||
MβCD [μM] | 0 β-A | 2.5 β-A | 0 β-A | 2.5 β-A |
0 | 121.8 ± 1.1 | 160 ± 30 | 129.1 ± 1.6 | 170 ± 30 |
0.5 | 119.9 ± 2.4 | 220 ± 9 | 125.0 ± 2.9 | 234 ± 12 |
1 | 123 ± 6 | 182 ± 16 | 128 ± 8 | 194 ± 20 |
1.5 | 123.1 ± 0.7 | 199 ± 9 | 129.3 ± 1.4 | 209 ± 10 |
2 | 122.3 ± 2.5 | 183 ± 23 | 129 ± 4 | 200 ± 30 |
2.5 | 131 ± 8 | 192 ± 26 | 138 ± 9 | 200 ± 30 |
t [min] = 90 | t [min] = 120 | |||
MβCD[μM] | 0 β-A | 2.5 β-A | 0 β-A | 2.5 β-A |
0 | 121.1 ± 1.8 | 150 ± 30 | 112.5 ± 2.5 | 141 ± 28 |
0.5 | 120.4 ± 2.4 | 217 ± 10 | 108.1 ± 0.9 | 203 ± 9 |
1 | 122 ± 7 | 187 ± 16 | 112 ± 5 | 168 ± 16 |
1.5 | 124 ± 4 | 203 ± 7 | 112 ± 4 | 185 ± 6 |
2 | 122 ± 4 | 217 ± 23 | 108 ± 4 | 167 ± 18 |
2.5 | 131 ± 8 | 196 ± 20 | 108 ± 5 | 175 ± 23 |
t [min] = 150 | t [min] = 180 | |||
MβCD [μM] | 0 β-A | 2.5 β-A | 0 β-A | 2.5 β-A |
0 | 111.1 ± 2.7 | 170 ± 30 | 108 ± 3 | 143 ± 23 |
0.5 | 105.5 ± 1.4 | 193 ± 8 | 101.8 ± 0.8 | 183 ± 7 |
1 | 108 ± 5 | 162 ± 15 | 103.5 ± 3.2 | 158 ± 12 |
1.5 | 109 ± 3 | 177 ± 7 | 104 ± 4 | 167 ± 8 |
2 | 104 ± 3 | 165 ± 24 | 99 ± 4 | 155 ± 19 |
2.5 | 107 ± 8 | 168 ± 22 | 101 ± 6 | 158 ± 19 |
t [min] = 210 | t [min] = 240 | |||
MβCD [μM] | 0 β-A | 2.5 β-A | 0 β-A | 2.5 β-A |
0 | 107 ± 4 | 140 ± 23 | 116 ± 4 | 155 ± 26 |
0.5 | 99.5 ± 1.5 | 178 ± 8 | 107.9 ± 2.0 | 197 ± 8 |