Sr. No | Properties | PVAc Homo | PVAc Homo CC | PVAc Homo CL |
1 | % Solid | 46.4 | 46.4 | 46.7 |
2 | Viscosity (Poise) | 400 | 320 | 500 |
3 | pH | 4.9 | 6.55 | 5.13 |
4 | Drying time on glass plate (% relative humidity-60% Temperature-30˚C) | 50 | 70 | 62 |
5 | Film Hardness | HB | 2H | 3H |
6 | Contact angle (˚) | 45.7 ± 1.39 | 43.2 ± 2.38 | 54.3 ± 2.92 |
7 | Glass transition temperature (˚C) | 106.10 | 111.18 | 118.89 |
8 | Tensile share strength (Dry) (MPa) |
|
|
|
4 hr | 1.86 ± 0.4 | 2.08 ± 0.4 | 2.09 ± 0.4 | |
6 hr | 3.27 ± 0.4 | 4.32 ± 0.4 | 4.17 ± 0.4 | |
24 hr | 4.56 ± 0.4 | 6.08 ± 0.4 | 5.70 ± 0.4 | |
7 Days | 6.20 ± 0.4 | 6.23 ± 0.4 | 6.23 ± 0.4 | |
9 | Tensile shear strength (Wet) (MPa) | 1.15 ± 0.3 | 1.10 ± 0.3 | 1.43 ± 0.3 |
After 24 hr |