Material | k-value mNµm3/2 | hkink (µm) | FN-kink (mN) | Wtransition mNµm/mN | Origin of Data |
Soda Lime Glass | 77.909 105.28 122.01 | 0.4925 0.7739 1.1173a) | 23.6782 58.9005 up to 120 mN | 0.1173 0.4744 0.6228b) | Oliver-Pharr 1992, J Mater Res 7, 1584 |
Al (only the experimental) | 9.7181 11.613 | 1.2105 2.0997a) | 12.1330 up to 32 mN | 0.1418 1.2095b) | K. Zeng, Acta Mater 2001, 49, 3539 |
Al (only data up to 90 mN) | 12.036 13.377 | 3.1086 3.8963a) | 60.4343 up to 90 mN | 0.2230 2.4958b) | Oliver-Pharr 1992, J Mater Res 7, 1584 |
Si (001), B-doped, p-type | 112.14c) 121.75 155.62 160.62 | 0.1501 0.2522 0.3309 0.4917a) | 6.5328 15.2899 25.2002 up to 50 mN | 0.00687 0.02687 0.1942 0.3014b) | T.F. Page, 1992, J Mater Res 7, 450 |
Si (100) | 123.2 145.44 151.53 | 0.4077 0.7245 0.81968a) | 29.1622 81.0015 up to 100 mN | 0.1545 0.4684 0.5659b) | S.V. Hainsworth 1996, J Mater Res 11, 1987 |