Subs-tance

Temperature range, K

η₁ and η₂, mPa·c

Е, J/mol

$\overline{a}$ , sh.u.

$E/\overline{a}$ , J/cluster

Е (34), J/mol

LiCl

Т_т− T_b

${\eta }_1=1.59{\left(910/T\right)}^a$

$а=3.6853{\left(980/T\right)}^{0.4703}$

${\eta }_2=3.43\times {10}^{-2}{\text{e}}^{\frac{29045}{RT}}$

29,045

3.298

8807

31,176

NaCl

Т_т− 1273

1273 − T_b

${\eta }_1=1.432{\left(1098/T\right)}^a$

$а=5.1792{\left(1173/T\right)}^{0.9261}$

${\eta }_2=6.493\times {10}^{-3}{\text{e}}^{\frac{49326}{RT}}$

${\eta }_2=2.175\times {10}^{-2}{\text{e}}^{\frac{36464}{RT}}$

49,326

36,464

5.193

3.94

9499

9255

49,089

37,245

KCl

Т_т − T_b

${\eta }_1=1.42{\left(1063/T\right)}^a$

$а=3.860{\left(1108/T\right)}^{0.8682}$

${\eta }_2=5.5\times {10}^{-2}{\text{e}}^{\frac{28546}{RT}}$

28,546

3.187

8957

30,127

AgCl

Т_т − T_b

${\eta }_1=2.29{\left(730/T\right)}^a$

$а=1.8047{\left(850/T\right)}^{0.4256}$

${\eta }_2=0.317\times {10}^{-2}{\text{e}}^{\frac{12039}{RT}}$

12,039

1.549

7772

14,643

NaF

Т_т − 1500

1500 − T_b

${\eta }_1=1.85{\left(1288/T\right)}^a$

$a=3.816{\left(1383/T\right)}^{0.893}$

${\eta }_2=4.416\times {10}^{-2}{\text{e}}^{\frac{39909}{RT}}$

${\eta }_2=7.746\times {10}^{-2}{\text{e}}^{\frac{32592}{RT}}$

39,909

32,592

3.825

3.131

10,433

10,409

36,158

29,597

KI

Т_т − T_b

${\eta }_1=1.53{\left(980/T\right)}^a$

$a=2.587{\left(1080/T\right)}^{0.353}$

${\eta }_2=8.892\times {10}^{-2}{\text{e}}^{\frac{23280}{RT}}$

23,280

2.451

9498

23,169

The average

−

−

31,400

3.322

9329

(31,403)